Material testing apparatus and procedures for evaluating freeze-thaw resistance of asphalt concrete mixtures

Chun-Hsing Ho, Cristina Pilar Martin Linares, Junyi Shan, Anas Almonnieay

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

This paper presents material testing procedures using an ASTM C666 (Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing) apparatus to evaluate resistance of asphalt concrete (AC) mixtures with respect to freezethaw (F-T) cycles. The ASTM C666 apparatus is mostly used for testing F-T resistance of pervious concrete, but it can be an ideal device to replace the currently used AASHTO T283, Standard Method of Test for Resistance of Compacted Asphalt Mixtures to Moisture-Induced Damage, as it was never intended to simulate F-T resistance for asphalt mixtures. To evaluate the effectiveness of the ASTM C666 apparatus in determination of F-T resistance of asphalt mixtures, two types of AC materials were sampled from an asphalt paving project: rubberized modified asphalt (RMA) and fiber reinforced asphalt (FRA). All specimens were prepared in the Materials Laboratory of Northern Arizona University, and their F-T resistance was tested using an ASTMC666 apparatus at six designed cycles: 0, 100, 150, 200, 250, and 300 cycles. After each desired cycle is complete, specimens were removed from the ASTM C666 apparatus and then tested for their stiffness using a bending beam rheometer (BBR). The viscoelastic reposes of asphalt mixtures tended to be less significant after 150 F-T cycles. The field evaluation of local asphalt paving associated with climatic F-T cycle data and F-T test results indicate that surface conditions and cracking progress of the asphalt pavements do have closer agreement with the increase of F-T cycles. The ASTM C666 apparatus is capable of providing F-T conditioning of the specimens. In combination of the BBR device and the corresponding procedure, the thermal properties of the mix (e.g., stiffness at 60 s or relaxation modulus function) can be measured and determined. The testing procedures and results are promising and prone to the purposes of F-T resistant simulation. The findings presented in this paper provide a positive trend for future research focusing on the evaluation of long-term F-T durability of asphalt mixtures.

Original languageEnglish (US)
Pages (from-to)429-443
Number of pages15
JournalAdvances in Civil Engineering Materials
Volume6
Issue number1
DOIs
StatePublished - Oct 30 2017

Fingerprint

asphalt
Materials testing apparatus
Asphalt mixtures
Asphalt concrete
Concrete mixtures
Asphalt
Rheometers
Stiffness
Concretes
Thawing
Materials testing
Asphalt pavements
Testing
Freezing
Durability
Moisture
Thermodynamic properties
Fibers

Keywords

  • Asphalt mixtures
  • ASTM C666 apparatus
  • Freeze-thaw cycles
  • Low temperature performance

ASJC Scopus subject areas

  • Ceramics and Composites
  • Civil and Structural Engineering
  • Mechanics of Materials
  • Polymers and Plastics
  • Metals and Alloys
  • Materials Chemistry

Cite this

Material testing apparatus and procedures for evaluating freeze-thaw resistance of asphalt concrete mixtures. / Ho, Chun-Hsing; Linares, Cristina Pilar Martin; Shan, Junyi; Almonnieay, Anas.

In: Advances in Civil Engineering Materials, Vol. 6, No. 1, 30.10.2017, p. 429-443.

Research output: Contribution to journalArticle

Ho, Chun-Hsing ; Linares, Cristina Pilar Martin ; Shan, Junyi ; Almonnieay, Anas. / Material testing apparatus and procedures for evaluating freeze-thaw resistance of asphalt concrete mixtures. In: Advances in Civil Engineering Materials. 2017 ; Vol. 6, No. 1. pp. 429-443.
@article{6c3288a9f57944afb09124df529dae18,
title = "Material testing apparatus and procedures for evaluating freeze-thaw resistance of asphalt concrete mixtures",
abstract = "This paper presents material testing procedures using an ASTM C666 (Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing) apparatus to evaluate resistance of asphalt concrete (AC) mixtures with respect to freezethaw (F-T) cycles. The ASTM C666 apparatus is mostly used for testing F-T resistance of pervious concrete, but it can be an ideal device to replace the currently used AASHTO T283, Standard Method of Test for Resistance of Compacted Asphalt Mixtures to Moisture-Induced Damage, as it was never intended to simulate F-T resistance for asphalt mixtures. To evaluate the effectiveness of the ASTM C666 apparatus in determination of F-T resistance of asphalt mixtures, two types of AC materials were sampled from an asphalt paving project: rubberized modified asphalt (RMA) and fiber reinforced asphalt (FRA). All specimens were prepared in the Materials Laboratory of Northern Arizona University, and their F-T resistance was tested using an ASTMC666 apparatus at six designed cycles: 0, 100, 150, 200, 250, and 300 cycles. After each desired cycle is complete, specimens were removed from the ASTM C666 apparatus and then tested for their stiffness using a bending beam rheometer (BBR). The viscoelastic reposes of asphalt mixtures tended to be less significant after 150 F-T cycles. The field evaluation of local asphalt paving associated with climatic F-T cycle data and F-T test results indicate that surface conditions and cracking progress of the asphalt pavements do have closer agreement with the increase of F-T cycles. The ASTM C666 apparatus is capable of providing F-T conditioning of the specimens. In combination of the BBR device and the corresponding procedure, the thermal properties of the mix (e.g., stiffness at 60 s or relaxation modulus function) can be measured and determined. The testing procedures and results are promising and prone to the purposes of F-T resistant simulation. The findings presented in this paper provide a positive trend for future research focusing on the evaluation of long-term F-T durability of asphalt mixtures.",
keywords = "Asphalt mixtures, ASTM C666 apparatus, Freeze-thaw cycles, Low temperature performance",
author = "Chun-Hsing Ho and Linares, {Cristina Pilar Martin} and Junyi Shan and Anas Almonnieay",
year = "2017",
month = "10",
day = "30",
doi = "10.1520/ACEM20170005",
language = "English (US)",
volume = "6",
pages = "429--443",
journal = "Advances in Civil Engineering Materials",
issn = "2379-1357",
publisher = "ASTM International",
number = "1",

}

TY - JOUR

T1 - Material testing apparatus and procedures for evaluating freeze-thaw resistance of asphalt concrete mixtures

AU - Ho, Chun-Hsing

AU - Linares, Cristina Pilar Martin

AU - Shan, Junyi

AU - Almonnieay, Anas

PY - 2017/10/30

Y1 - 2017/10/30

N2 - This paper presents material testing procedures using an ASTM C666 (Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing) apparatus to evaluate resistance of asphalt concrete (AC) mixtures with respect to freezethaw (F-T) cycles. The ASTM C666 apparatus is mostly used for testing F-T resistance of pervious concrete, but it can be an ideal device to replace the currently used AASHTO T283, Standard Method of Test for Resistance of Compacted Asphalt Mixtures to Moisture-Induced Damage, as it was never intended to simulate F-T resistance for asphalt mixtures. To evaluate the effectiveness of the ASTM C666 apparatus in determination of F-T resistance of asphalt mixtures, two types of AC materials were sampled from an asphalt paving project: rubberized modified asphalt (RMA) and fiber reinforced asphalt (FRA). All specimens were prepared in the Materials Laboratory of Northern Arizona University, and their F-T resistance was tested using an ASTMC666 apparatus at six designed cycles: 0, 100, 150, 200, 250, and 300 cycles. After each desired cycle is complete, specimens were removed from the ASTM C666 apparatus and then tested for their stiffness using a bending beam rheometer (BBR). The viscoelastic reposes of asphalt mixtures tended to be less significant after 150 F-T cycles. The field evaluation of local asphalt paving associated with climatic F-T cycle data and F-T test results indicate that surface conditions and cracking progress of the asphalt pavements do have closer agreement with the increase of F-T cycles. The ASTM C666 apparatus is capable of providing F-T conditioning of the specimens. In combination of the BBR device and the corresponding procedure, the thermal properties of the mix (e.g., stiffness at 60 s or relaxation modulus function) can be measured and determined. The testing procedures and results are promising and prone to the purposes of F-T resistant simulation. The findings presented in this paper provide a positive trend for future research focusing on the evaluation of long-term F-T durability of asphalt mixtures.

AB - This paper presents material testing procedures using an ASTM C666 (Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing) apparatus to evaluate resistance of asphalt concrete (AC) mixtures with respect to freezethaw (F-T) cycles. The ASTM C666 apparatus is mostly used for testing F-T resistance of pervious concrete, but it can be an ideal device to replace the currently used AASHTO T283, Standard Method of Test for Resistance of Compacted Asphalt Mixtures to Moisture-Induced Damage, as it was never intended to simulate F-T resistance for asphalt mixtures. To evaluate the effectiveness of the ASTM C666 apparatus in determination of F-T resistance of asphalt mixtures, two types of AC materials were sampled from an asphalt paving project: rubberized modified asphalt (RMA) and fiber reinforced asphalt (FRA). All specimens were prepared in the Materials Laboratory of Northern Arizona University, and their F-T resistance was tested using an ASTMC666 apparatus at six designed cycles: 0, 100, 150, 200, 250, and 300 cycles. After each desired cycle is complete, specimens were removed from the ASTM C666 apparatus and then tested for their stiffness using a bending beam rheometer (BBR). The viscoelastic reposes of asphalt mixtures tended to be less significant after 150 F-T cycles. The field evaluation of local asphalt paving associated with climatic F-T cycle data and F-T test results indicate that surface conditions and cracking progress of the asphalt pavements do have closer agreement with the increase of F-T cycles. The ASTM C666 apparatus is capable of providing F-T conditioning of the specimens. In combination of the BBR device and the corresponding procedure, the thermal properties of the mix (e.g., stiffness at 60 s or relaxation modulus function) can be measured and determined. The testing procedures and results are promising and prone to the purposes of F-T resistant simulation. The findings presented in this paper provide a positive trend for future research focusing on the evaluation of long-term F-T durability of asphalt mixtures.

KW - Asphalt mixtures

KW - ASTM C666 apparatus

KW - Freeze-thaw cycles

KW - Low temperature performance

UR - http://www.scopus.com/inward/record.url?scp=85042693007&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85042693007&partnerID=8YFLogxK

U2 - 10.1520/ACEM20170005

DO - 10.1520/ACEM20170005

M3 - Article

VL - 6

SP - 429

EP - 443

JO - Advances in Civil Engineering Materials

JF - Advances in Civil Engineering Materials

SN - 2379-1357

IS - 1

ER -